Description
Weld metal having lesser impurities i.e. S, P, will improve the subzero impact property and retains its mechanical properties after prolonged heat treatments. Ideal for welding similar composition materials. The weld metal displays excellent tensile strength and creep resistance. Specially applicable wherever the impact o property requirement at subzero temperatures up to minus 20 C.
Approvals
BHEL
CE
CHEMICAL COMPOSITION OF ALL WELD METAL (%)
|
Element |
C | Mn | Si | S | P | Cr | Mo | Sn | As | Sb |
|
Percent |
0.06 | 0.76 | 0.49 | 0.007 | 0.010 | 1.25 | 0.50 | 0.002 | 0.004 | 0.002 |
MECHANICAL PROPERTIES OF ALL WELD METAL
| UTS | YS | Elongation |
CVN Impact Strength (J) |
CVN Impact Strength (J) |
Creep Strength at 550°C |
| (MPa) |
(MPa) |
(L= 5d)% |
at Minus -20°C |
20°C |
(1%offset in 10,000 hrs) |
| 620 | 530 | 22 |
80 |
100 |
120 MPa |
DIFFUSIBLE HYDROGEN CONTENT: 5 ml/100 gms of weld metal (max.).
CURRENT AND PACKING DATA: DC (+)
|
Size (mm) |
6.3x450 | 5x450 | 4x350 |
3.15x350 |
2.5x350 |
|
Current Range (Amps) |
250-300 | 200-250 | 140-180 |
100-130 |
70-100 |
|
Qty. (Pcs./Carton) |
25 | 30 | 50 |
75 | 100 |