Description
A non-synthetic nickel base electrode, depositing weld metal of Ni-Cr-Mo-Co-Ti-W alloys. The weld deposit resists corrosion resistance at room temperature as well as resistance to oxidation and reducing atmospheres at elevated temperatures. Electrodes are used for welding Ni-Cr-Mo alloy, for the welding of the clad side of joints in steel clad with Ni-Cr-Mo alloy, and for joining Ni-Cr-Mo alloys to steel and to other nickel base alloys. Some of the materials, which are welded with these electrodes, are ASTM B 574, B 575, B 619, B 622 and B 626 having UNS number N 06985.
Approvals
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
|
Element |
C | Mn | Si | S | P | Fe | Ni | Cr | Mo | Co | Ti | W |
|
Percent |
0.012 | 0.90 | 0.12 | 0.020 | 0.024 | 2.5 | 64.3 | 15.0 | 15.0 | 1.50 | 0.20 | 0.40 |
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL
| UTS | Elongation |
| (MPa) |
(L= 4d)% |
| 725 | 31.0 |
CURRENT AND PACKING DATA: AC / DC(+)
|
Size (mm) Dia x Length |
5x350 | 4x350 |
3.15x350 |
2.5x350 |
|
Current Range (Amps) |
150-180 | 120-150 |
80-110 |
60-70 |
|
Weight / Carton (kgs) |
2.5 | 2.5 |
2.5 |
2.5 |